В настоящей работе для увеличения прочности сцепления плазменно-напыленных покрытий применена обработка непрерывным CO2 - лазером и приведены результаты исследования влияния различных режимов вводимой мощности на структуру, фазовый и химический состав, микротвердость формирующихся покрытий.

The influence of continious CO2-laser processing on structure, composition and microhadness of plasma sprayed Ni-Cr-Si-B, Fe-C-Cr-V, Ni-Al coatings was studied. The change of chemical and phase compositions of the coatings compared with the initial sprayed ones due to alloying with elements of substrate, depending on the processing operation (input power) was determined. Laser processing of plasma sprayed coatings allows to improve substantially their adhesion and in combination with high speed cooling, gives the possibility to regulate the processes of structure formation, dispersion, phase formation, and hence, the properties of forming coatings by means of processing operation.

Предмет "Технология конструкционных материалов" является одной из инженерных дисциплин, основы которой используются при курсовом и дипломном проектировании, а также в практической деятельности специалистов технического профиля. Он продолжает курс "Материаловедение" и должен сформировать глубокие знания по технологии производства и обработке конструкционных материалов, современные представления о научно-техническом прогрессе в области получения и использования новых материалов, совершенствования технологических процессов. На этой основе должны быть выработаны умения и навыки практического определения физико-механических свойств материалов и направленного воздействия на них. Методические указания и контрольные задания разработаны на основе типовой программы курса с учетом особенностей подготовки специалистов в ЯГУ.